In the present work, NaI – LiBH4 system fabricated by ball milling were post annealed and their variation of Li+ ion conductivity were investigated. From the change of lattice parameters by post annealing, it was suggested that unreacted LiBH4 existed in as-milled sample further dissolved into NaI, which implied an enhancement of the sample homogeneity. On the other hand, the segregation of LiI was anticipated when ball milled 15NaI·LiI (BH4 free sample) was annealed at 423 K. Li+ conductivity was decreased by post anneal process and compositional dependence of an activation energy for Li+ conduction was indicated for the homogeneous NaI – LiBH4 system.